Flexible Barrier Manufacturing Poised for Takeoff
Dr Harry Zervos
SEP 09, 2015 13:48 PM
A+ A A-

Flexible Barrier Manufacturing Poised for Takeoff

By Dr Harry Zervos, IDTechEx Research

A large opportunity lies in the development of devices in a flexible form factor that can operate without deterioration in performance, allowing them to be more robust, lightweight and versatile in their use ― such as in wearable technology. This is specifically related to flexible OLED displays, and other devices using organic materials (such as OPV), where the organic materials deteriorate very quickly with exposure to oxygen and water.

Flexible devices are a key differentiating component in consumer electronics and automotive applications and, therefore, the flexible encapsulation technology has been under intense development by many companies worldwide.

Status of Flexible Encapsulation to Enable Flexible Electronics

By 2020 flexible barrier manufacturing for flexible electronic devices, such as displays, will be a market worth more than US $184 million. That equates to 3.8 million square meters of flexible barrier films for electronics.

Although multilayer approaches – usually organic and inorganic layers - have been the most popular solution for flexible encapsulation so far, there is significant development work with solutions based on single layer approaches, such as flexible glass or atomic layer deposition (ALD) which could, in later years, capture part of the market. The table below shows some of the characteristics of flexible glass and ALD films as developers are looking to bring them to market. 

ALD and Flexible Glass Metrics and Commercialization Status for Beneq, Lotus and Corning

Company Name

WVTR (gr/sq.m./day

Deposition Technique

Material

Commercialization Status - Strategy

Beneq

Can reach

10-6

Batch ALD. Also developing roll 2 Roll ALD.

Proprietary Aluminium Oxide/Titanium Oxide nanolaminate

Beneq supplies coating equipment

Lotus

Can reach

10-6

Roll 2 Roll ALD

Proprietary homogeneous mixture" of Aluminium Oxide/Titanium Oxide layers

Lotus follows a licensing business model and is patenting Plasma Enabled Oxygen Radical Decomposition process so as to enable faster deposition rates

Corning

Perfect sealing from water vapour/oxygen

Down drawing

Thin glass (less than 100 μm)

Available in rolls and sheets, in sample volumes

 

Source: IDTechEx report, “Barrier Layers for Flexible Electronics 2015-2025” www.IDTechEx.com/barrier

Flexible Glass: Current Status, Outlook and Challenges

Flexible glass is a significant technical achievement yet it will not be the solution of choice for encapsulation of flexible electronics in the short- to medium-term, for multiple reasons.

First, in spite of manufacturers’ marketing spin, glass is inherently a fragile material and requires specialized handling and processing. While plastic materials can also be damaged, there is an important difference between the two: damage of barriers on plastic can lead to the failure of a specific part, however, shattering of glass, even if protective sheets are used, leads to particle contamination on the defect line that can affect multiple parts.

This inherent fragility of flexible glass makes sheet edges critical. All suppliers propose protective tabs to reduce the problem, however, any other particle on the processing equipment could also become a focal point of stress and lead to shattering of the glass sheet or web.

A strong point of traditional glass encapsulation (especially for top emission devices) has been its ability to form truly hermetic packaging by using glass frit and laser sealing. This advantage may be not transferable to flexible glass where glass-to-glass sealing may be very problematic and difficult because points of stress and relative twisting of the two sheets must be avoided in the laser firing of the frit. It may be that flexible glass has to be used in combination with adhesives (and desiccants).

Flexibility is another issue. Although glass is very flexible, if it’s flexed along a well-defined axis it can be poor at tolerating any stress out of axis, so much so that twisting the sheet may lead to fracture. This is true with or without protective film applied to the glass. Extreme flexibility (r< 2-3 mm) may also be a problem. Current data shows the flexibility limit around r= 2.5 cm. Consequently, flexible glass as an encapsulant superstrate or substrate may be good for conformal applications, but for truly flexible applications there seem to be several challenges to overcome.

Flexible glass makers are also waiting for equipment providers to make appropriate equipment to handle the flexible glass in manufacturing ― another bottle neck.

Future Opportunities for Flexible Glass

 The thermal stability of flexible glass makes it the best choice as substrate for backplanes of high-resolution, high-end large displays. Glass enables improved resolution and good registration between layers during processing compared to plastic substrates like PET, PEN, and PI. However, IDTechEx analysts and other affiliate experts have only seen results with metal oxide backplanes only so far (Tprocess < 350C), none with LTPS backplanes (Tprocess < 450C). If processability up to 450C is indeed possible, flexible glass would be a very good choice as a substrate for flexible AMOLED TV. Those devices are bottom emission (BE) AMOLED, and normally have a metal foil as back encapsulant and a higher cost tolerance.  Manufacturing by R2R will require specialized tools not different than fabrication of barrier in R2R.

The multi-layer approach, if correctly implemented on dedicated tools, may have the potential to be low cost but an open question remains as to how low the defect density of barrier on foil can be. Consequently, it is an open question what the maximum size of displays that can be encapsulated with compatible yield can be.  Plastic engineered superstrate (encapsulant foil) may be better for smaller devices (wearables, phones, tablets), while flexible glass may be better for TVs and ― in general ― larger displays.

Additionally, the smoothness of plastic films, even with smoothing layers, is not as good as glass (0.2 nm). This may be a problem for organic TFT backplanes. Finally optical transmission below 400nm require glass as substrate since PET and PEN have a cut off around 400 nm (PEN).

Atomic Layer Deposition (ALD): Present and Future Market Share

Atomic Layer Deposition (ALD) is another flexible encapsulation technology receiving a lot of attention, with several players currently developing solutions based on it. It seems like it is not a short-term solution, if it will ever be one as a stand-alone layer, but ALD may be a solution in a multi-layer stack in combination with a sputtered or PECVD layer if it would be possible to find a good cost structure. Regarding the intrinsic properties of the material, ALD film deposited at low temperature (T<80C) have a superior quality when tested at room temperature. A single ALD layer less-than 50 nm thick can perform better than thicker layers deposited by sputtering or PECVD.

However, the inherent stability of the films at higher temperature/humidity (e.g. 85C/85%RH) is a problem. If PECVD is used, ALD film stability improves, as well as for mixed oxides, but it is still an issue. A second problem comes with the non-uniformity of particles and substrates. Any defect may lead at an initial non-uniform nucleation that propagates into the growing film. Furthermore, loose particles on substrates may be partially covered, but because of the extreme thinness, the thin film does not have the mechanical strength to keep them in place under mechanical stress. Any mechanical stress leads to film fracture with consequent creation of an ingress path for moisture. That is why multi-layer structures are necessary.

Deposition tools are in development from Lotus, Beneq, Encapsulix and others. Exploration at Samsung SDC with ALD films for TFE was very much advertised by Synos, but resulted in failure and any further evaluation was halted. ALD for barrier on foil has better results although there are doubts and hurdles in scaling up and reaching the deposition speed required for a cost-effective process.

In The IDTechEx report, “Barrier Layers for Flexible Electronics 2015-2025,” provides full analysis of the topic, including 10- year forecasts by each application type and profiles of the key suppliers (www.idtechex.com/barrier).

The subject will also be covered in more detail at the Printed Electronics USA event, which will be held on Nov.18-19, 2015 in Santa Clara, California. See www.PrintedElectronicsUSA.com for full details.

FIRST
PREV
NEXT
LAST
Page(s):
[%= name %]
[%= createDate %]
[%= comment %]
Share this:
Please login to enter a comment:
RESET

Computing Now Blogs
Business Intelligence
by Drew Hendricks
by Keith Peterson
Cloud Computing
A Cloud Blog: by Irena Bojanova
The Clear Cloud: by STC Cloud Computing
Careers
Computing Careers: by Lori Cameron
Display Technologies
Enterprise Solutions
Enterprise Thinking: by Josh Greenbaum
Healthcare Technologies
The Doctor Is In: Dr. Keith W. Vrbicky
Heterogeneous Systems
Hot Topics
NealNotes: by Neal Leavitt
Industry Trends
The Robotics Report: by Jeff Debrosse
Internet Of Things
Sensing IoT: by Irena Bojanova